成型收缩率：1.4/2.0mm(具体见物性大全)
密度：1.15
UL94阻燃：UL94V-0/0.82mm(具体见物性大全)
描述：注塑阻燃
Zytel® FR7026V0F NC010
Zytel® FR7026V0F NC010 is a flame retardant polyamide 66 resin for injection molding. It does not contain elemental phosphorous, halogens or heavy metals.
| Property | Test Method | Units | Value | ||
| DAM | 50%RH | ||||
| Identification | |||||
| Resin Identification | ISO 1043 | PA66-FR(30) | |||
| Part Marking Code | ISO 11469 | >PA66-FR(30)< | |||
| Mechanical | |||||
| Yield Stress | ISO 527 | MPa (kpsi) | |||
| 50mm/min | 90 (13) | 60 (9) | |||
| Yield Strain | ISO 527 | % | |||
| 50mm/min | 4 | 21 | |||
| Stress at Break | ISO 527 | MPa (kpsi) | 90 (13) | ||
| Strain at Break | ISO 527 | % | 14 | ||
| Nominal Strain at Break | ISO 527 | % | 5 | 30 | |
| Tensile Modulus | ISO 527 | MPa (kpsi) | 3750 (540) | 1800 (260) | |
| Notched Charpy Impact Strength | ISO 179/1eA | kJ/m2 | |||
| -30°C (-22°F) | 3 | 2 | |||
| 23°C (73°F) | 4 | 7 | |||
| Unnotched Charpy Impact Strength | ISO 179/1eU | kJ/m2 | 80 | 110 | |
Contact DuPont for Material Safety Data Sheet, general guides and/or additional information about ventilation, handling, purging, drying, etc. ISO Mechanical properties measured at 4.0mm, ISO Electrical properties measured at 2.0mm, and all ASTM properties measured at 3.2mm. Test temperatures are 23°C unless otherwise stated.
During molding, use proper protective equipment and adequate ventilation. Avoid exposure to fumes and limit the hold up time and temperature of the resin in the machine. Purge degraded resin carefully with HDPE.
Zytel® FR7026V0F NC010
| Property | Test Method | Units | Value | ||||
| DAM | 50%RH | ||||||
| Thermal | |||||||
| Deflection Temperature | ISO 75-1/-2 | °C (°F) | |||||
| 1.80MPa | 70 | (158) | |||||
| Melting Temperature | ISO 11357-1/-3 | °C (°F) | |||||
| 10°C/min | 263 (505) | ||||||
| Electrical | |||||||
| CTI | IEC 60112 | PLC | 0 | ||||
| CTI | UL 746A | PLC | 0 | ||||
| Flammability | |||||||
| Flammability Classification | IEC 60695-11-10 | ||||||
| 0.82mm | V-0 | ||||||
| 1.5mm | V-0 | ||||||
| 3.0mm | V-0 | ||||||
| Flammability Classification | UL94 | ||||||
| 0.82mm | V-0 | ||||||
| 1.5mm | V-0 | ||||||
| 3.0mm | V-0 | ||||||
| Oxygen Index | ISO 4589-1/-2 | % | 39 | ||||
| High Current Arc Ignition Resistance | UL 746A | PLC | |||||
| 0.82mm | 0 | ||||||
| 1.5mm | 0 | ||||||
| 3.0mm | 0 | ||||||
| High Voltage Arc Tracking Rate | UL 746A | PLC | |||||
| 0.82mm | 0 | ||||||
| 1.5mm | 0 | ||||||
| 3.0mm | 0 | ||||||
| Hot Wire Ignition | UL 746A | PLC | |||||
| 0.82mm | 3 | ||||||
| 1.5mm | 3 | ||||||
| 3.0mm | 2 | ||||||
Zytel® FR7026V0F NC010
| Property | Test Method | Units | Value | |||
| DAM | 50%RH | |||||
| Temperature Index | ||||||
| RTI, Electrical | UL 746B | °C | ||||
| 0.82mm | 130 | |||||
| 1.5mm | 130 | |||||
| 3.0mm | 130 | |||||
| RTI, Impact | UL 746B | °C | ||||
| 0.82mm | 95 | |||||
| 1.5mm | 95 | |||||
| 3.0mm | 95 | |||||
| RTI, Strength | UL 746B | °C | ||||
| 0.82mm | 110 | |||||
| 1.5mm | 110 | |||||
| 3.0mm | 110 | |||||
| Other | ||||||
| Density | ISO 1183 | kg/m3 (g/cm3) | 1150 (1.15) | |||
| Molding Shrinkage | ISO 294-4 | % | ||||
| Normal, 2.0mm | 1.4 | |||||
| Parallel, 2.0mm | 1.2 | |||||
| Mold Shrinkage | % | |||||
| Flow, 1.6mm (0.062in) | 0.8 | |||||
| Flow, 3.2mm (0.125in) | 1.1 | |||||
| Transverse, 1.6mm (0.062in) | 0.8 | |||||
| Transverse, 3.2mm (0.125in) | 1.1 | |||||
| Processing | ||||||
| Melt Temperature Range | °C (°F) | 270-290 (520-555) | ||||
| Melt Temperature Optimum | °C (°F) | 280 (535) | ||||
| Mold Temperature Range | °C (°F) | 50-90 (120-190) | ||||
| Mold Temperature Optimum | °C (°F) | 70 (160) | ||||
| Drying Time, Dehumidified Dryer | h | 2-4 | ||||
| Drying Temperature | °C (°F) | 80 (175) | ||||
| Processing Moisture Content | % | <0.20 | ||||